Figure 1 – uploaded by Ratnamala Chatterjee

See full PDFdownloadDownload figure
Lattice parameter ‘a’ for Mn,Nio.s_.ZMNo,sFe2O4 ferrites Table |

Table 1 Lattice parameter ‘a’ for Mn,Nio.s_.ZMNo,sFe2O4 ferrites Table |

Related Figures (4)

Fig. 1. X-ray diffractogram of Mno,.2Nio,3Zno.sFe204 powder calcined at 500°C. The electromagnetic properties obtained for Mn-Ni~Zn ferrites are shown in Table 2. As seen in the Table, the DC-resistivity, p, of the ferrites is of the order of about 10*Q-cm. The value of
Fig. 1. X-ray diffractogram of Mno,.2Nio,3Zno.sFe204 powder calcined at 500°C. The electromagnetic properties obtained for Mn-Ni~Zn ferrites are shown in Table 2. As seen in the Table, the DC-resistivity, p, of the ferrites is of the order of about 10*Q-cm. The value of
Properties of Mn,Nio,s_.Zno.sFe2O4 ferrites Table 2
Properties of Mn,Nio,s_.Zno.sFe2O4 ferrites Table 2
Power loss of Mn,Nio,s_.ZNo,sFe2O4 ferrites under different conditions of frequency, magnetic field and temperature
Power loss of Mn,Nio,s_.ZNo,sFe2O4 ferrites under different conditions of frequency, magnetic field and temperature
Fig. 2. Frequency variation of initial perrmeability (u) and loss factor (tan 0) of Mno 2Nig 3ZNo,5FexO4 F
Fig. 2. Frequency variation of initial perrmeability (u) and loss factor (tan 0) of Mno 2Nig 3ZNo,5FexO4 F
Related topics:
Mechanical EngineeringCondensed Matter PhysicsEddy CurrentCurie temperatureMagnetism and Magnetic MaterialsSwitch Mode Power Supplies